| Standardization: | Numberical Symbol: | |
| GB/T9460-2008 | SCu6511 | |
| BS EN14640:2005 | Cu 6511 |
|
| GB Chemical Composition: | % | |
| Cu incl.ag | bal. | |
| Zn | max 0.20 | |
| Sn | 0.10-0.30 | |
| Mn | 0.50-1.50 | |
| Fe | max 0.10 | |
| Si | 1.50-2.00 | |
| P | max 0.02 | |
| Al | max 0.01 | |
| Pb | max 0.02 | |
| Total others | max 0.5 | |
| Physical properties of materials: | ||
| Density | Kg/m^3 | 8.7 |
| Melting range | ℃ | 1030-1050 |
| Thermal conductivity | W/m.K | 40 |
| Electrical conductivity | S.m/mm^2 | 4.7-5.3 |
| Coefficient of thermal expansion | 10^-6/K(20-300℃) | 18.1 |
| Standard values of the weld metal: | ||
| Elongation | % | 40 |
| Tensile strength | N/mm^2 | 280 |
| Notched bar impact work | J | 70 |
| Brinell hardness | HB 2.5/62.5 | 61 |
| Applications: | ||
| Particularly suitable for MIG brazing of zinc coated sheets in the car engineering,good flowing properties of weld pool,low tendency to porosity and spatter,also suitable for welding of zinc alloys, large work pieces preheating is recommended.For multilayer welding low alloyed copper,for low and unalloyed steels and cast iron.For large work pieces preheating is recommended.Ideal for the use in car body making. | ||
| Make up: | ||
| Diameter:0.64 - 0.80 - 1.00 - 1.20 - 1.60 -2.40 | ||
| Spools:D100,D200,D300,D760,K300,KS300 |
||
| Rods:1.60 - 9.6 mm x 914/1000 mm |
||
| Further make ups on request. |
||